Keser, SerhatKaya, SemihBarzinjy, Azeez A.Mahmood, Bahroz KareemKareem, Rebaz ObaidTemuz, Mehmet MursitBulut, Niyazi2026-06-192026-06-1920261820-61312406-1034https://hdl.handle.net/20.500.12899/6260In this study, hydroxyapatite (HAp) samples, co-doped with 0.44 at.% of zinc and different amount of quercetin (Zn/Que-HAp), were synthesised using a wet-chemical method and calcined at 900 degrees C. XRD shows HAp as the primary phase with minor beta-TCP. Compared to the Zn-doped sample without quercetin (Q1), quercetin co-doping induces clear structural changes (shifts of lattice parameters a from-0.0017 to +0.0006 nm and c from-0.0026 to-0.0005 nm), accompanied by changes in crystallinity (from-3.6% to +2.5%) and crystallite size (from-3.5 to +0.6 nm), evidencing a distinct co-doping effect. DTA/TGA reveal reduced total mass loss for the Que-containing compositions relative to the Zn-doped sample, indicating enhanced thermal stability of the co-doped lattice. SEM reveals granular morphologies with interconnected porosity, while EDX yields (Ca+Zn)/P ratios greater than 1.67, consistent with Ca-sufficient apatite and modified defect chemistry. DFT calculations resolve the site-specific effects of Zn substitution and predict a preference for perturbation at Ca2 sites. The electronic density of states retains a wide-gap, insulating character, with localised states sensitive to the dopant configuration. By correlating experiment and theory, we demonstrate that the organic-inorganic co-dopant pair offers an effective means to tune lattice metrics, phase balance, and thermal response without compromising the intrinsic insulating nature of HAp.eninfo:eu-repo/semantics/closedAccessHydroxyapatiteDopingBioceramicsThermal AnalysisCrystal StructureArticle20137482-s2.0-105040514374Q3WOS:001735788800005Q4